| Description |
Fabricant |
Pays |
No. CE |
standard |
Composition |
Fiches de sécurité |
| METAUX POUR COURONNE COULEE |
|
|
|
|
|
|
| Non précieux |
|
|
|
|
|
|
| 4ALL |
Ivoclar |
Liechtenstein |
CE0123 |
ISO 9693 |
Ni61.4 Cr25.7 Mo11 Si1.5 Mn<1.0 Al<1 C<1 |
 |
| Non précieux Chrome Cobalt |
|
|
|
|
|
|
| Wirobond 280 |
Bego |
Allemagne |
CE0044 |
ISO 9693 |
Co60,2 Cr25 Mo4,8 W6,2 Ga2,9 Si Mn |
|
| Titane |
|
|
|
|
|
|
| Girotan L |
Bego |
Allemagne |
CE0044 |
ISO 9693 |
Ti 87 Nb 7 Al 6 |
|
| Semi précieux |
|
|
|
|
|
|
| Pallorag 33 |
Cendres et métaux |
Suisse |
CE0510 |
ISO 8891 |
Au+Pt 30 Au10 Pd20 Ag59,2 Cu9,5 Zn1 |
|
| Précieux |
|
|
|
|
|
|
| Academy Gold |
Williams |
Etats-Unis |
CE0197 |
ISO 8891 |
Au77,2 Ag12,7 Cu8,5 Ir In Pt Zn Ta |
|
| XL-X |
Williams |
Etats-Unis |
CE0197 |
ISO 8891 |
Au62,8 Ag16,1 Cu15,7 Pd3,9 Zn1 1r1 |
|
| METAUX POUR CERAMIQUE |
|
|
|
|
|
|
| Non précieux |
|
|
|
|
|
|
| 4ALL |
Ivoclar |
Liechtenstein |
CE0123 |
ISO 9693 |
Ni 61.4 Cr 25.7 Mo 11 Si 1.5 |
|
| Non précieux Chrome Cobalt |
|
|
|
|
|
|
| Wirobond 280 |
Bego |
Allemagne |
CE0044 |
ISO 9693 |
Co 60,2 Cr 25 Mo 4,8 W 6,2 Ga 2,9 |
|
| Titane |
|
|
|
|
|
|
| Girotan L |
AmannGirrbach |
Allemagne |
CE0044 |
ISO 9693 |
Ti 87 Nb 7 Al 6 |
|
| Semi précieux |
|
|
|
|
|
|
| d.Sign 53 |
Ivoclar |
Liechtenstein |
CE0197 |
ISO 9693 |
Pd 53,8 Ag 34,9 Sn 7,7 Zn 1,2 In 1,7 |
|
| Précieux |
|
|
|
|
|
|
| d.Sign 98 |
Ivoclar |
Liechtenstein |
CE0197 |
ISO 9693 |
Au 85,9 Pt 12,1 Zn 1,5 |
|
| CERAMIQUE SUR ARMATURE |
|
|
|
|
|
|
| Sur non précieux |
|
|
|
|
|
|
| Ips In Line |
Ivoclar |
Liechtenstein |
CE 0123 |
ISO 9693 |
SiO 98 BaO Al2O3 CaO CeO2 |
|
| Vmk 95 |
Vita |
Allemagne |
CE 0124 |
ISO 9693 |
|
|
| Sur non précieux Chrome Cobalt |
|
|
|
|
|
|
| Ips In Line |
Ivoclar |
Liechtenstein |
CE 0123 |
ISO 9693 |
SiO2 98 BaO Al2O3 CaO |
|
| Sur titane |
|
|
|
|
|
|
| Triceram |
Dentaurum |
Allemagne |
ISO 9693 |
|
Synthetic vitroceranmic powder with Sio2, Al2o3, k2o, Na2O, li2O, BaO, Mgo, B2O3, F |
|
| Semi précieux et précieux |
|
|
|
|
|
|
| Ips In Line |
Ivoclar |
Liechtenstein |
CE 0123 |
ISO 9693 |
SiO2 98 BaO Al2O3 CaO CeO2 |
|
| COMPOSITE |
|
|
|
|
|
|
| Ceramage |
Shofu |
Japon |
CE 0044 |
|
|
|
| CERAMIQUE-CERAMIQUE |
|
|
|
|
|
|
| Cérmique pressée |
|
|
|
|
|
|
| Empress Esthetic |
Ivoclar |
Liechtenstein |
CE 0123 |
ISO 6872 |
> 97 % SiO2 < 3 % TiO2 pigments |
|
| Emax |
Ivoclar |
Liechtenstein |
CE 0124 ISO 6872 |
|
<50%SiO2, CaO, Al2O3, CeO2, Na2O, K2O, B2O3, ZnO, F, Li2O, ZrO2, P2O5, SrO, TiO2 and pigment |
|
| In Ceram |
Vita |
Allemagne |
CE 0124 ISO 6872 |
|
|
|
| Allceram (Procera system) |
Degudent |
Allemagne |
CE 0483 |
ISO 6872 |
|
|
| Triceram (Cercon system) |
Degudent |
Allemagne |
ICE 0483 |
ISO 9693 |
Synthetic vitroceranmic powder with Sio2, Al2o3, k2o, Na2O, li2O, BaO, Mgo, B2O3, F |
|
 |
|
|
|
|
|
|